Alumina -Reinforced Friction Stir Processing for Enhanced ۶۰۶۱ Aluminum Performance
- سال انتشار: 1404
- محل انتشار: اولین همایش بین المللی پژوهش های کاربردی در مهندسی
- کد COI اختصاصی: ENGSCOS01_026
- زبان مقاله: انگلیسی
- تعداد مشاهده: 69
نویسندگان
M.Sc. graduate, Department of Mechanical Engineering, Islamic Azad University Tabriz Branch, Tabriz, Iran
B.Sc. student, Department of Petroleum Engineering, Faculty of Engineering, Urmia University, Urmia, Iran
B.Sc. graduate, Department of Mechanical Engineering, Islamic Azad University Khoy Branch, Khoy, Iran
PhD student, Manufacturing Group, Faculty of Mechanic, Tabriz University, Tabriz, Iran
B.Sc. graduate, Department of Mechanical Engineering, Faculty of Engineering, Qazvin University, Iran
B.Sc. graduate, Department of Manufacturing, Faculty of Mechanical Engineering, Shahid Rajaee Teacher Training University, Tehran, Iran
چکیده
This study investigates the fabrication and characterization of surface composites on ۶۰۶۱ aluminum alloy using Friction Stir Processing (FSP) with and without alumina (Al₂O₃) reinforcement. The effects of micron- and nano-sized alumina particles on mechanical properties, microhardness, and corrosion resistance were systematically evaluated. FSP was carried out using custom-designed tools and fixtures, and alumina powders were incorporated into the stir zone through a pre-machined groove and zigzag hole pattern. Three processing conditions were explored: FSP without reinforcement (FSP(NP)), FSP with micron-sized alumina (FSP/Al₂O₃(M)), and FSP with nano-sized alumina (FSP/Al₂O₃(N)). The sample reinforced with micron-sized alumina exhibited the highest ultimate tensile strength (۲۱۴ MPa) and yield strength (۱۳۰ MPa), representing improvements of ۲۶% and ۶% over the base alloy, respectively. Microhardness also increased significantly, reaching ۹۰ HV for micron-reinforced samples compared to ۴۶ HV in the base metal. Electrochemical corrosion testing in ۳.۵ wt.% NaCl solution revealed superior performance in the micron-reinforced sample, which exhibited the lowest corrosion current density (۱.۸۸ × ۱۰⁻⁵ A/cm²) and corrosion rate (۰.۲۶۴۵ mm/year), along with the highest polarization resistance (۱۴۷۳ Ω). The findings confirm that FSP enhances the mechanical and corrosion-resistant properties of aluminum alloys, particularly when reinforced with micron-sized alumina. These improvements position FSP as a viable surface modification technique for demanding applications in aerospace, automotive, and marine industries where wear and corrosion resistance are critical.کلیدواژه ها
مقالات مرتبط جدید
- تشخیص لینک مخرب با استفاده از TF-IDF و رگرسیون لجستیک
- چالشها و راهکارهای امنیتی در شبکه های بدون سرور با استفاده از فناوری بلاکچین
- Exploring Frameworks of Information Behavior and Informal Learning: A Narrative Review Across Leisure, Equity, AI, and Cross-Cultural Contexts
- Self-Directed Language Learning and Information Behavior in Leisure Time: An International Comparative Study of Duolingo Use Among Iranian and Canadian EFL Learners
- ارائه یک سیستم توصیه گر مبتنی بر پیشنهاد محصول به مشتری در فروشگاه های اینترنتی با یادگیری ماشین
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.