Post-Fire Behavior of Post-Tensioned Segmental Concrete Beams under Monotonic Static Loading
- سال انتشار: 1399
- محل انتشار: ژورنال مهندسی عمران، دوره: 6، شماره: 5
- کد COI اختصاصی: JR_CEJ-6-5_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 36
نویسندگان
Civil Engineering Department, College of Engineering, University of Baghdad,, Iraq
Civil Engineering Department, College of Engineering, University of Baghdad,, Iraq
Civil Engineering Department, Al-Farabi University College,, Iraq
چکیده
This paper presents a study to investigate the behavior of post-tensioned segmental concrete beams that exposed to high-temperature. The experimental program included fabricating and testing twelve simply supported beams that divided into three groups depending on the number of precasting concrete segments. All specimens were prepared with an identical length of ۳۱۵۰ mm and differed in the number of the incorporated segments of the beam (۹, ۷, or ۵ segments). To simulate the genuine fire disasters, nine out of twelve beams were exposed to a high-temperature flame for one hour. Based on the standard fire curve (ASTM – E۱۱۹), the temperatures of ۳۰۰â—¦C (۵۷۲â—¦F), ۵۰۰â—¦C (۹۳۲â—¦F), and ۷۰۰â—¦C (۱۲۹۲â—¦F) were adopted. Consequently, the beams that exposed to be cool gradually under the ambient laboratory condition, after that, the beams were loaded till failure to investigate the influence of the heating temperature on the performance during the serviceability and the failure stage. It was observed that, as the temperature increased in the internal layers of concrete, the camber of tested beams increased significantly and attained its peak value at the end of the time interval of the stabilization of the heating temperature. This can be attributed to the extra time that was consumed for the heat energy to migrate across the cross-section and to travel along the span of the beam and deteriorate the texture of the concrete causing microcracking with a larger surface area. Experimental findings showed that the load-carrying capacity of the test specimen, with the same number of incorporated concrete segments, was significantly decreased as the heating temperature increased during the fire event.This paper presents a study to investigate the behavior of post-tensioned segmental concrete beams that exposed to high-temperature. The experimental program included fabricating and testing twelve simply supported beams that divided into three groups depending on the number of precasting concrete segments. All specimens were prepared with an identical length of ۳۱۵۰ mm and differed in the number of the incorporated segments of the beam (۹, ۷, or ۵ segments). To simulate the genuine fire disasters, nine out of twelve beams were exposed to a high-temperature flame for one hour. Based on the standard fire curve (ASTM – E۱۱۹), the temperatures of ۳۰۰â—¦C (۵۷۲â—¦F), ۵۰۰â—¦C (۹۳۲â—¦F), and ۷۰۰â—¦C (۱۲۹۲â—¦F) were adopted. Consequently, the beams that exposed to be cool gradually under the ambient laboratory condition, after that, the beams were loaded till failure to investigate the influence of the heating temperature on the performance during the serviceability and the failure stage. It was observed that, as the temperature increased in the internal layers of concrete, the camber of tested beams increased significantly and attained its peak value at the end of the time interval of the stabilization of the heating temperature. This can be attributed to the extra time that was consumed for the heat energy to migrate across the cross-section and to travel along the span of the beam and deteriorate the texture of the concrete causing microcracking with a larger surface area. Experimental findings showed that the load-carrying capacity of the test specimen, with the same number of incorporated concrete segments, was significantly decreased as the heating temperature increased during the fire event.کلیدواژه ها
Segmental Beam Post-tensioning Fire Test Gradual Cooling Serviceability Load Capacity.اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.