Introduction of CaCO۳ as Electron Recombination Barrier Layer in TiO۲-Based Dye-Sensitized Solar Cell

سال انتشار: 1404
محل انتشار: مجله مواد دوستدار محیط، دوره: 9، شماره: 1
کد COI اختصاصی: JR_JEFM-9-1_005
زبان مقاله: انگلیسی
تعداد مشاهده: 13

نویسندگان

Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran

چکیده

Calcium carbonate (CaCO۳) is an effective material for surface modification in TiO۲-based dye-sensitized solar cells (DSSCs).Its higher conduction band position compared to TiO۲ helps reduce electron recombination rates, and its elevated isoelectricpoint promotes increased dye adsorption. It is crucial to control the thickness of the CaCO۳ layer to less than ۳-۱۰ nm, astunneling phenomena cannot occur when the insulating layer exceeds ۱۰ nm in thickness. In this study, the CaCO۳ layer wasdeposited using the spin-coating method. Additionally, in two samples, the second TiCl۴ treatment was omitted during DSSCpreparation to assess its impact on the photovoltaic properties. The results indicate that while the deposition of CaCO۳ enhancesthe photocurrent of the DSSCs, it simultaneously reduces the fill factor. However, applying the TiCl۴ treatment both beforeand after CaCO۳ deposition improves the fill factor, leading to greater efficiency compared to the untreated samples.Specifically, sample TT۳CT achieved an efficiency of ۷.۹۸%, while the neat sample reached ۷.۵۸% efficiency.

کلیدواژه ها

DSSC, Surface Modification, Recombination Barrier Layer, Calcium Carbonate

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.