Enhancing Superconducting Properties of Thallium-Based Tl-۱۲۲۳ Thin Films through Optimized Rapid Thermal Annealing of Titanium Alloy Precursor Films on Lanthanum Aluminate Substrates
- سال انتشار: 1403
- محل انتشار: Iranian Journal of Chemistry and Chemical Engineering، دوره: 43، شماره: 12
- کد COI اختصاصی: JR_IJCCE-43-12_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 226
نویسندگان
Key Laboratory of New Electrical Functional Materials in Guangxi Universities, Nanning Normal University, Nanning, P.R. CHINA
Key Laboratory of New Electrical Functional Materials in Guangxi Universities, Nanning Normal University, Nanning, P.R. CHINA
Key Laboratory of New Electrical Functional Materials in Guangxi Universities, Nanning Normal University, Nanning, P.R. CHINA
Key Laboratory of New Electrical Functional Materials in Guangxi Universities, Nanning Normal University, Nanning, P.R. CHINA
Key Laboratory of New Electrical Functional Materials in Guangxi Universities, Nanning Normal University, Nanning, P.R. CHINA
چکیده
This paper shows the enhancements of a Tl-۱۲۲۳ high-temperature superconducting thin film prepared on lanthanum aluminate (LAO) substrates using an optimized rapid thermal annealing process. The annealing process of the precursor film was improved, and the effects of different annealing conditions on the thalliation crystallization of the precursor film were investigated. A precursor film of the Tl-based high-temperature superconducting thin film was first prepared on the surface of the LAO substrate using the magnetron sputtering process, followed by annealing treatment in a rapid thermal furnace. X-Ray Diffraction (XRD) characterization showed that both the annealing temperature and the heating rate significantly affect the phase formation of the precursor film. Through annealing optimizations, films with a Tc of ۱۱۵K and Jc of ۲.۲ MA/cm۲ were achieved, demonstrating enhanced superconducting performance. By adjusting the parameters, a Tl-۱۲۲۳ superconducting thin film with a highly oriented c-axis can be fabricated. Scanning Electron Microscopy (SEM) observations indicated that the superconducting films with good crystalline states have smooth and intact surface morphology, and the critical transition temperature (Tc) of the superconducting films prepared was measured at about ۱۱۵K in liquid nitrogen. The films’ crystallinity was gauged using Atomic Force Microscopy (AFM) for three-dimensional information.کلیدواژه ها
Tl-۱۲۲۳ Superconducting Thin Film, Optimized rapid thermal annealing process, Lanthanum aluminate, magnetron sputteringاطلاعات بیشتر در مورد COI