Modeling of hot deformation behavior and processing map of ۱۳-۸Mo precipitation hardening steel
- سال انتشار: 1403
- محل انتشار: هفتمین کنفرانس بین المللی جوشکاری وغیرمخرب، بیست و پنجمین کنفرانس ملی جوش و بازرسی، چهاردهمین کنفرانس ملی آزمایش های غیرمخرب و سومین کنفرانس ملی ساخت افزایشی
- کد COI اختصاصی: INCWI25_045
- زبان مقاله: انگلیسی
- تعداد مشاهده: 374
نویسندگان
Master's Student, Metallurgy and Materials Engineering, Malek Ashtar University of Technology, Esfahan
Assistant Professor, Metallurgy and Materials Engineering, Malek Ashtar University of Technology, Esfahan
چکیده
The objective of this research is to model the hot deformation behavior and draw processing map for ۱۳-۸Mo steel. For this purpose, hot compression tests were conducted on cylindrical samples with a diameter of ۵ mm and a height of ۱۰ mm within a temperature range of ۸۵۰ to ۱۱۵۰°C and strain rates from ۰.۰۰۱ to ۱s⁻¹. The microstructure of the deformed samples obtained from the hot compression tests was examined using optical microscopes.According to the results, as temperature increases and strain rate decreases, the flow stress decreases. Flow curves were plotted to estimate the constants of the fundamental power relationship at various strains. Based on fundamental calculations, the activation energy for this steel was determined to be ۲۸۸.۶۲ kJ/mol. Subsequently, processing map were drawn for strain rates ranging from ۰.۱ to ۰.۷. It was found that in the temperature range of ۱۰۷۰ to ۱۱۵۰°C and strain rates between ۰.۱ and ۰.۱۵s⁻¹, dynamic recrystallization occurs with an efficiency of Power dissipation between ۰.۲ and ۰.۵۲.Additionally, the results from the processing map indicated the presence of one unstable region and two stable regions for deformation; investigations revealed that there is kinking and shear band in the microstructure, which is attributed to the unstable region and dynamic recrystallization being the main factor for stability.کلیدواژه ها
۱۳-۸Mo precipitation hardening steel, Dynamic recrystallization, Hot compression test, Processing map, Characteristic equations.مقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.