Introduction of CaCO۳ as Electron Recombination Barrier Layerin TiO۲-based Dye-Sensitized Solar Cell

سال انتشار: 1403
محل انتشار: سیزدهمین کنفرانس بین المللی مهندسی مواد و متالورژی
کد COI اختصاصی: IMES18_149
زبان مقاله: انگلیسی
تعداد مشاهده: 176

نویسندگان

Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran

چکیده

Calcium carbonate (CaCO۳) is an effective material for surface modification in TiO۲-based dye-sensitized solarcells (DSSCs). Its higher conduction band position compared to TiO۲ helps reduce electron recombination rates,and its elevated isoelectric point promotes increased dye adsorption. It is crucial to control the thickness of theCaCO۳ layer to less than ۳-۱۰ nm, as tunneling phenomena cannot occur when the insulating layer exceeds ۱۰nm in thickness. In this study, the CaCO۳ layer was deposited using the spin-coating method. Additionally, intwo samples, the second TiCl۴ treatment was omitted during DSSC preparation to assess its impact on thephotovoltaic properties. The results indicate that while the deposition of CaCO۳ enhances the photocurrent ofthe DSSCs, it simultaneously reduces the fill factor. However, applying the TiCl۴ treatment both before andafter CaCO۳ deposition improves the fill factor, leading to greater efficiency compared to the untreatedsamples. Specifically, sample TT۳CT achieved an efficiency of ۷.۹۸%, while the neat sample reached ۷.۵۸%efficiency.

کلیدواژه ها

DSSC, Surface Modification, Recombination Barrier Layer, Calcium Carbonate

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.