Morphological Investigation of Al-Cu-Fe Quasi-Crystalline Thin Film on Ti-۶Al-۴V Alloy
- سال انتشار: 1403
- محل انتشار: مجله ی بین المللی انجمن آهن و فولاد ایران، دوره: 21، شماره: 1
- کد COI اختصاصی: JR_ISSIRAN-21-1_002
- زبان مقاله: انگلیسی
- تعداد مشاهده: 142
نویسندگان
Materials and Energy Research Center (MERC)
Materials and Energy Research Center (MERC)
Materials and Energy Research Center (MERC)
Materials and Energy Research Center (MERC)
چکیده
Magnetron sputtering was used in the current study to deposit the quasicrystal (QC) coating on the Ti-۶Al-۴V alloy. After the sputtering process, a continuous argon flow at ۷۰۰°C was used for two hours to anneal the Al-Cu-Fe coated samples. The microstructure and morphology of mixed powders and Al-Cu-Fe QC coatings were examined using scanning electron microscope (SEM) analysis and X-ray diffraction (XRD). The Al۶۲.۵Cu۲۵Fe۱۲.۵ powder mixing was used as the target of the magnetic sputtering process. Al-Cu-Fe thin layer's deposition on the Ti-۶Al-۴V alloy surface took place with no cracks and a thickness of approximately ۴۰۰۰ nm. As shown by calculations, five facet shapes had a size of nearly ۶۴۳ nm. The XRD patterns confirmed the presence of Al۳Fe, AlTi۲, and Al۶۵Cu۲۰Fe۱۵ phases after the post-heat treatment coating.کلیدواژه ها
Quasicrystals, Thin film, Ti-۶Al-۴V alloyاطلاعات بیشتر در مورد COI