Effect of SiC Content on the Microstructure of Semi-solid A356/SiCp Composite Castings Processed via Vibrating Cooling Slope Method

سال انتشار: 1390
محل انتشار: دوازدهمین کنفرانس ملی مهندسی ساخت و تولید ایران
کد COI اختصاصی: ICME12_108
زبان مقاله: انگلیسی
تعداد مشاهده: 782

نویسندگان

School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran,

چکیده

The aim of this paper is to study the effect of SiC content on semi-solid processing of A356-SiCp composite using a relatively new process termed Vibrating Cooling Slope (VCS) method. In this study, for the first time, VCS method was used for processing of A356-SiCp composites and the effect of SiC content (in the range of 0-20 vol. %) for a fixed SiC particle size (76μm) on the microstructure of solidified alloy and composites was investigated. It was concluded that by pouring the molten A356 metal on the vibrating cooling slope with desired length, angle, frequency and amplitude, globular structures could be directly achieved. By increasing the SiC content, the average diameter of globules decreased at the expense of decreased shape factor. However, a more uniform distribution of SiC particles within the matrix alloy was achieved for increased SiC content.

کلیدواژه ها

Semi-solid casting, Composite, Vibrating cooling slope, Average diameter, Shape factor, Distribution factor

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.