Heat Treatment of a (Ti,Hf)-Rich NiTiHf High Temperature Shape Memory Alloy

  • سال انتشار: 1390
  • محل انتشار: دوازدهمین کنفرانس ملی مهندسی ساخت و تولید ایران
  • کد COI اختصاصی: ICME12_020
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 1098
دانلود فایل این مقاله

نویسندگان

M Moshref-Javadi

School of Materials & Metallurgical Engineering, Iran University of Science & Technology, Tehran, Iran

M Belbasi

School of Materials & Metallurgical Engineering, Iran University of Science & Technology, Tehran, Iran

S. H. Seyedein

School of Materials & Metallurgical Engineering, Iran University of Science & Technology, Tehran, Iran

M. T. Salehi

School of Materials & Metallurgical Engineering, Iran University of Science & Technology, Tehran, Iran

چکیده

NiTiHf alloys are known as one of the most promising groups of shape memory alloys for operating at temperatures above 100 ºC. In this paper, effect of intermediate aging on the microstructure, transformation temperatures, and one-way shape memory behavior of a Ni49Ti36Hf15 alloy was investigated. For this purpose, an ingot was fabricated using vacuum induction melting of high purity Ni, Ti, and Hf precursors. The alloy was then homogenized at 1000 ºC, hot-rolled at 850 ºC, and solution treated at 1000 ºC, respectively, to be prepared for aging treatment. Aging treatment was carried out at 500 ºC and 600 ºC for 2h. OM, SEM, XRD, DSC, and the so-called bending test were used to characterize the alloy. Results demonstrated that microstructure of the aged Ni49Ti36Hf15 is composed of B19’ martensitic matrix, (Ti,Hf)2Ni second phase mostly at grain boundary regions, and a new phase, while an approximately 25 ºC decrease in transformation temperatures was observed after aging. It was also found that this heat treatment cannot provide better shape memory properties for the alloy. That aging provided no improvement was correlated to the microstructure of the alloy.

کلیدواژه ها

Aging; Heat treatment; High temperature shape memory alloy; Martensite; Microstructure; NiTi; Shape memory effect; Transformation temperatures

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.