Realization of Fiber reinforced Composite Materials Based on Damaging Mechanisms

سال انتشار: 1390
محل انتشار: دوازدهمین کنفرانس ملی مهندسی ساخت و تولید ایران
کد COI اختصاصی: ICME12_010
زبان مقاله: انگلیسی
تعداد مشاهده: 853

نویسندگان

Faculty of Mechanical Engineering, University of Tabriz, Tabriz, Iran

چکیده

The cracks by intralaminar decohesion in composite materials appear a little ahead of the delamination front under the action of triaxial stresses before any decohesion at the interfaces between layers. The actual phenomenon of delamination is caused by previous damaging of the resin ahead of the front resulting first in the formation of intralaminar cracks. The microscopic mechanisms involve numerous changes of planes formation during delamination, so that delamination cannot he considered, in any case, as a simple decohesion between two adjacent layers. Analysis of damaging mechanisms supported by scanning electron microscope (SEM) observations gave useful information about the conception and design of long fiber reinforced composite materials. In this paper after a synthesis on the mechanisms of fracture of composite materials by delamination which were proved by SEM photographs, suggestions have been given for realization of these materials.

کلیدواژه ها

Composite material; Crack; Delamination; Damaging mechanism

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.