Design and synthesis of polyuethane membranes with different hard to softsegment ratio

  • سال انتشار: 1403
  • محل انتشار: شانزدهمین سمینار بین المللی علوم و تکنولوژی پلیمر (ISPST ۲۰۲۴)
  • کد COI اختصاصی: ISPST16_615
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 76
دانلود فایل این مقاله

نویسندگان

S. Jamalpour

Department of Chemical Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz (SCU),Ahvaz, Iran

R. Bavi

Department of Chemical Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz (SCU),Ahvaz, Iran

M. Salehzadeh

Department of Chemical Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz (SCU),Ahvaz, Iran

چکیده

The polyurethane polymer were prepared by solvent polymerization. Structural characteristics of themembranes were studied by X-ray diffraction to confirm the interactions between PU segments. TheXRD analysis of synthesized PUs shows higher peak intensity in PU-۴:۱:۳ due to a higher percentageof hard segments, indicating increased crystallinity.

کلیدواژه ها

Hard-to-soft segment ratio, Polyurethane, solvent polymerization, membrane

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.