Effect of Electron Beam Irradiation on Physical and Mechanical Propertiesof Bakelite Valves

  • سال انتشار: 1403
  • محل انتشار: شانزدهمین سمینار بین المللی علوم و تکنولوژی پلیمر (ISPST ۲۰۲۴)
  • کد COI اختصاصی: ISPST16_597
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 58
دانلود فایل این مقاله

نویسندگان

Mustafa Mohammadi

Department of Polymer Engineering, Shiraz Branch, Islamic Azad University, Shiraz, Iran, ۷۱۹۸۷-۷۴۷۳۱

Gholam-Reza Nejabat

Department of Polymer Engineering, Shiraz Branch, Islamic Azad University, Shiraz, Iran, ۷۱۹۸۷-۷۴۷۳۱۲Department of Applied Researches, Chemical, Petroleum & Polymer Engineering Research Center, ShirazBranch, Islamic Azad University, Shiraz, Iran, ۷۱۹۸۷-۷۴

M. SadeghTavallali

Department of Chemical Engineering, Shiraz Branch, Islamic Azad University, Shiraz, Iran, ۷۱۹۸۷-۷۴۷۳۱۴Department of Advanced Calculations, Chemical, Petroleum & Polymer Engineering Research Center, ShirazBranch, Islamic Azad University, Shiraz, Iran, ۷۱۹۸

M Mehdi Rasti

Fars Province Gas Company (FPGC), Shiraz, Fars, Iran

چکیده

Bakelite valves are used in diaphragm gas meters. In this research various Bakelite valve speciesare exposed to ۱۲ MeV electron beam irradiation (EBI) at two doses of ۶۰ and ۸۰ kGy. Theirradiations are done under vacuum at room temperature and the effects are studied via FTIR,SEM, TGA, tensile and impact tests. The results show that at ۶۰ kGy, physical and mechanicalproperties of the samples enhance while at ۸۰ kGy deteriorate or do not change considerably. FTIRshow that the -OH peak disappears upon irradiation at both doses. SEM proves the appearance ofdeffects on samples at ۸۰ kGy. TGA shows enhancement in thermal behavior of the samplesespecially at ۶۰ kGy. Impact strenght experiences considerable improvements especially at ۶۰ kGy(+۱۸۰% ) while tensile strenght improves a little at the same dose (+۲%) and deteriarates at ۸۰ kGy(-۳۴%). It can be said that EBI at ۶۰ kGy improves the said physical and mechanical properties ofthe samples while by increasing the dose to ۸۰ kGy the properties start to detoriorate.

کلیدواژه ها

Characterizatin of Bakelite, Polymer modification, Electron beam irradiation (EBI).

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.