Synthesis of Mg-MOF-۷۴ at ambient temperature and its use in Mg-MOF-۷۴/polyurethane mixed matrix membrane for gas separation

سال انتشار: 1403
محل انتشار: شانزدهمین سمینار بین المللی علوم و تکنولوژی پلیمر (ISPST ۲۰۲۴)
کد COI اختصاصی: ISPST16_436
زبان مقاله: انگلیسی
تعداد مشاهده: 124

نویسندگان

Department of Chemical Engineering, Isfahan University of Technology, Po. Box ۸۴۱۵۶-۸۳۱۱۱, Isfahan, Iran.

چکیده

In the current study, Mg-MOF-۷۴ crystals were synthesized and characterized at ambient temperature as aprecursor for the development of mixed-matrix membranes (MMMs) with a polymer matrix for efficientCO۲/N۲ separation. The primary objective was to incorporate these Mg-MOF-۷۴ crystals into a polyurethanematrix to fabricate dense MMMs using a solvent casting technique. To evaluate their gas separationcapabilities, CO۲ and N۲ permeability tests were conducted at a controlled pressure of ۴ bar, maintainingsteady-state conditions.The gas permeability results revealed an enhancement in CO۲ permeability with theincrease in MOF loading up to a threshold of ۵ wt%, beyond which a decline was observed in the ۱۰ wt%membrane. Conversely, the CO۲/N۲ selectivity displayed a negative correlation with MOF content,indicating the exceptional adsorptive selectivity of Mg-MOF-۷۴ towards CO۲ molecules.

کلیدواژه ها

Polymer Membranes, Gas separation, Polyurethane, Mixed matrix membranes, Metalorganic frameworks

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.