Effect of Adding LDPE, PP and Biodegradable Plastic Waste on Physical Properties, Calorific Value and Proximate Analysis of Peanut Shell Waste Briquettes
- سال انتشار: 1404
- محل انتشار: ماهنامه بین المللی مهندسی، دوره: 38، شماره: 1
- کد COI اختصاصی: JR_IJE-38-1_006
- زبان مقاله: انگلیسی
- تعداد مشاهده: 130
نویسندگان
Department of Petroleum Engineering, Faculty of Technology Earth and Energy, Universitas Trisakti, Jakarta, Indonesia
Department of Petroleum Engineering, Faculty of Technology Earth and Energy, Universitas Trisakti, Jakarta, Indonesia
Department of Petroleum Engineering, Faculty of Technology Earth and Energy, Universitas Trisakti, Jakarta, Indonesia
Department of Mining Engineering, Faculty of Technology Earth and Energy, Universitas Trisakti, Jakarta, Indonesia
Department of Petroleum Engineering, Faculty of Technology Earth and Energy, Universitas Trisakti, Jakarta, Indonesia
Department of Petroleum Engineering, Faculty of Technology Earth and Energy, Universitas Trisakti, Jakarta, Indonesia
Department of Electrical Engineering, College of Engineering and Agro-Industrial Technology, University of the Philippines Los Baños, Philippines
چکیده
Peanut shell (PS) waste and plastic waste are abundant in Indonesia and have the potential to pollute the environment. The limited availability of fossil fuels also makes all parties look for other energy sources. This research aims to find a solution to this problem. The effect of adding low density polyethylene (LDPE), polypropylene (PP), and biodegradable plastic to briquettes made from peanut shell waste was investigated in this research. Briquettes were made using starch adhesive and a compaction pressure of ۷۰ N/m۲ using a laboratory scale piston. The compression test is essential because, during the stacking process, the briquettes must withstand loads from external pressure, which significantly influences the quality of the briquettes during storage and transportation. This research found that adding biodegradable plastic increased the modulus of elasticity and compressive strength of briquettes, namely ۲۰ MPa and ۴.۴۵ MPa, compared to briquettes without plastic. The highest calorific value of briquettes in this study was obtained from the addition of PP plastic, amounting to ۶۱۸۵ cal/g. Based on the quality of the briquettes, the lowest moisture content was obtained from the addition of LDPE plastic at ۷.۷۱%, and the lowest ash content was obtained from the addition of biodegradable plastic at ۴.۰۱%, the lowest volatile content was obtained from the addition of PP plastic amounting to ۱۵.۷۱%. The most considerable fixed carbon content was obtained from adding PP plastic, amounting to ۸۰.۲۵%.کلیدواژه ها
Biomass, Briquette, Compressive strength, Plastic Waste, Proximate analysisاطلاعات بیشتر در مورد COI