Hydrolysis of cellulose in the presence of TiO2 and TiO2–SiO2 mixed-oxide under microwave irradiation
- سال انتشار: 1392
- محل انتشار: دومین همایش ملی علوم و صنایع غذایی
- کد COI اختصاصی: GHOCHANFOOD02_450
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1501
نویسندگان
Department of Chemistry, Quchan Branch, Islamic Azad University, Quchan, Iran.
چکیده
The hydrolysis reaction of cellulose was studied under microwave irradiation in presence TiO2 and TiO2-SiO2. The TiO2-SiO2 nanocatalysts with different molar ratio ofTi/Si were successfully prepared via sol-gel process. An exception to catalytic activity was observed for nanocatalyst with a 70 mol% of Ti/Si. It was found that calcinationtemperature strongly affected its reactivity. The suitable calcinations temperature for TiO2 was at 450 ºC, whereas that for TiO2-SiO2 was 700 ºC. The highest product yield was observed at a hydrolysis temperature of 220 ºC for 10 min irradiation tim.The weight ratio of cellulose: catalyst was examined that best weight ratio was 1:0.1 in which the carbohydrate in reaction mixture reached to 6582.37 ppm.کلیدواژه ها
Cellulose; glucose; hydrolysis; TiO2-SiO2 nanocatalyst; microwaveمقالات مرتبط جدید
- بهینه سازی شاخص های رنگی پودر پروتئین شاهدانه
- اصلاح ساختار فیزیکوشیمیایی ژلاتین استخراج شده از ضایعات ماهی هوور توسط افزودن آگار
- Evaluation of antimicrobial and mechanical properties of potato starch and whey protein edible films incorporated with nisin
- The effect of pasteurization process and additives on the shelf life of Doogh
- بررسی اثر روغن سیاهدانه بر خواص فیزیکی فیلم صمغ فارسی
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.