Strength evaluations for treated peat with cement and polypropylene fibres using CBR tests

  • سال انتشار: 1391
  • محل انتشار: هفتمین سمپوزیوم بین المللی پیشرفتهای علوم و تکنولوژی
  • کد COI اختصاصی: SASTECH07_067
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 1023
دانلود فایل این مقاله

نویسندگان

Kalantari

Department of Civil Engineering, University of Hormozgan, Bandar Abbas, Iran

A Prasad

۲Department of Civil Engineering, Banaras Hindu University, Varanasi, India

چکیده

Peat or organic soils are those types of soils that contain a significant amount of organic material derived from plants or animals. Although peat deposits create obvious topographic features such as swamp and bogs, others are buried underground, having been covered with inorganic alluvial soils. These often are difficult to detect and are the source of differential settlements when subjected to loads from civil engineering projects..This article describes a laboratory study on treating peat using ordinary Portland cement (OPC) as binding agent and polypropylene fibers as additive. Due to high initial water content of peat, the usual moist curing technique used to cure the treated peat samples is not used and air curing method is used instead. Beside routine laboratory tests on plain peat, strength evaluation test on the treated peat samples with cement and fibres used in the research was California bearing ratio (CBR). Air curing period used was 90 days for the CBR (soaked and un-soaked) test samples. Various amounts of cements ( 15, 30 and 50%) as well as 0.15% of fibres were used to treat plain peat samples. The result of CBR tests show significant strength improvement of stabilized peat through curing period. Also as the cement amounts increase, treated samples gain more strength, while polypropylene fibers when added to the treated peat with cement not only give more strength values, rather contribute a considerable amount of uniformity and intactness to the cement treated peat samples as well.

کلیدواژه ها

Cement, Polypropylene fibers, Stabilization, California Bearing Ratio, Air curing

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.