Investigation of machinability of AISI 1045 Steel under Rolled, annealed, normalized and quench-tempered conditions

سال انتشار: 1391
محل انتشار: همایش ملی مهندسی مکانیک
کد COI اختصاصی: EASTTEHRANMECH02_083
زبان مقاله: انگلیسی
تعداد مشاهده: 1257

نویسندگان

Department of Metallurgy, Faculty of Engineering, University of Ferdowsi of Mashhad, Iran

چکیده

In this paper, machinability of AISI 1045 steels was studied in rolled, annealed, normalized, and quenchtemperedconditions. Machinability in turning was investigated based on cutting force and surface roughness. The microstructure of as received and Heat treated samples has been investigated by optical microscopy. Hardness and tensile tests was carried out on samples. Turning tests were performed at a depth of cut of 0.5mm, a feed rate of 0.05mm/rev, and cutting speeds of 13.89, 19.73, 27.79, 39.46 and 55.58m/min and dry conditions. Results show that the values of cutting force and surface roughness were in range 100 to 220N and 1 to 5μm, respectively. Quench-tempered sample shows the highest cutting force, while it shows the lowest surface roughness. As received sample has the lowest cutting force. By annealing and normalizing heat treatments, cutting force does no different significantly, but surface roughness increase.

کلیدواژه ها

Machinability, Heat treatment, AISI 1045 steels, Cutting force, Surface roughness

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.