Investigation of the Crystallinity and Morphology of Copolymer-Templated TitaniumDioxide Layer

سال انتشار: 1403
محل انتشار: بیست و دومین کنگره بین المللی شیمی انجمن شیمی ایران
کد COI اختصاصی: NICEC22_480
زبان مقاله: انگلیسی
تعداد مشاهده: 159

دانلود فایل این مقاله

نویسندگان

Ghazale Kazemi

Department of Chemistry, Catalysis Division, University of Isfahan, Isfahan ۸۱۷۴۶-۷۳۴۴۱, Iran.

v Mirkhani

Department of Chemistry, Catalysis Division, University of Isfahan, Isfahan ۸۱۷۴۶-۷۳۴۴۱, Iran.

r Keshavarzi

Department of Chemistry, Catalysis Division, University of Isfahan, Isfahan ۸۱۷۴۶-۷۳۴۴۱, Iran.

m Moghadam

Department of Chemistry, Catalysis Division, University of Isfahan, Isfahan ۸۱۷۴۶-۷۳۴۴۱, Iran.

s Tangestaninejad

Department of Chemistry, Catalysis Division, University of Isfahan, Isfahan ۸۱۷۴۶-۷۳۴۴۱, Iran.

I. Mohammadpoor-Baltork

Department of Chemistry, Catalysis Division, University of Isfahan, Isfahan ۸۱۷۴۶-۷۳۴۴۱, Iran.

چکیده

Titanium dioxide (TiO۲) is an attractive option for electron transport in optoelectronic devices due toits unique properties. In this study, the crystallinity and pores morphology of copolymer-templated titaniumdioxide were investigated. Using the P۱۲۳ block copolymer as a sacrificing template, a warm-like structure ofmesoporous was formed. This mesoporous layer was characterized using XRD, UV-vis, and FE-SEM methods

کلیدواژه ها

Templated mesoporous TiO۲ layer; Electron-transport layer (ETL); TiO۲ crystallinity; P۱۲۳ blockcopolymer.

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.