Investigating the Effect of Changing Plasma Electrolytic Oxidation on the Scratch Degradation of Ti-۶Al-۴V
- سال انتشار: 1403
- محل انتشار: مجله مواد دوستدار محیط، دوره: 8، شماره: 1
- کد COI اختصاصی: JR_JEFM-8-1_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 189
نویسندگان
Advanced Materials Engineering Research Center, Karaj Branch, Islamic Azad University, Karaj, Iran
Advanced Materials Engineering Research Center, Karaj Branch, Islamic Azad University, Karaj, Iran
Faculty of Technology and Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
Faculty of Materials Science and Engineering Khajeh Nasir Toosi University, Tehran. Iran
چکیده
In this research, plasma electrolytic oxidation (PEO) was prepared at duty voltage of ۳۵۰ and ۴۵۰ V and processing time of ۵and ۱۰ minutes on Ti-۶Al-۴V alloy in Na۲SiO۳ + KOH electrolyte. Then, the adhesion strength and microstructuraldegradation of the coating surface were investigated through a constant load scratch test, field-emission scanning electronmicroscope (FE-SEM), and X-ray diffraction (XRD), respectively. The results showed that while increasing the processingtime and duty voltage, the density of porosity and the amount of rutile on the coating surface increased. Meanwhile,microstructure degradations like delamination, gross spallation, and buckling spallation decreased due to increased adhesionstrength. This resulted from an increase in voltage and processing time.کلیدواژه ها
Plasma Electrolytic Oxidation (PEO), Ti۶Al۴V Alloy, Scratch Test, Degradation Mechanismsاطلاعات بیشتر در مورد COI