Experimental evaluation of green engineered cementitious composites.

سال انتشار: 1403
محل انتشار: اولین کنفرانس بین المللی تبادل اطلاعات علمی در زمینه مصالح و سازه های بتنی
کد COI اختصاصی: ICCNC01_046
زبان مقاله: انگلیسی
تعداد مشاهده: 184

نویسندگان

Kharazmi University, Tehran, Iran

چکیده

Engineered Cementitious Composites (ECCs), also known as bendable concrete, are special type offiber-reinforced materials that possess strain-hardening capabilities and compared to materials such asFRPs, have far higher bending and tensile strengths. The tests carried out in this study include slump tests,as well as tests concerning the mechanical properties of hardened concrete, namely compressive tests,bending tests.The results show that the mixture design containing ۷۵% PVA fibers has the highest averagecompressive strength, yielding ۲۸-day and ۹۰-day compressive strengths of ۷۲.۱۸ MPa and ۸۸.۸۴ MPa,respectively. The highest ۲۸-day and ۹۰-day bending strengths are equal to, respectively, ۱۲.۸۵ MPa and۱۴.۹۱ MPa, and correspond to the mixture design with ۱% of fiber content. These values indicate an increaseof roughly ۲۷.۷۵% compared to the control mixture design. Adding fibers to the mixture improves thetensile strength and hardening behavior of ECCs. Considering that the material is used instead of cement,it can be called green concrete.

کلیدواژه ها

Engineered cementitious composite(ECC), Green concrete, Flexural concrete, PVA,Poly vinyl alcohol, fly ash, PP, High strength.

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.