Analysis of changes in the severity of plastic shrinkage cracking in concrete mixtures under influenced of the addition of macro synthetic fibres

سال انتشار: 1403
محل انتشار: اولین کنفرانس بین المللی تبادل اطلاعات علمی در زمینه مصالح و سازه های بتنی
کد COI اختصاصی: ICCNC01_015
زبان مقاله: انگلیسی
تعداد مشاهده: 244

نویسندگان

Master Graduate, Highway and Transportation Engineering, School of Civil Engineering, Islamic AzadUniversity Tehran-North Branch, Tehran, Iran

Hanieh Motevali Kasmaee

Bachelor Graduate, Civil Engineering, School of Civil Engineering, Mazandaran-Pardisan University,Mazandaran, Iran

Seyed Javad Vaziri Kang Olyaei

Master Graduate, Highway and Transportation Engineering, Iran University of Science and Technology, Tehran,Iran

چکیده

Plastic shrinkage cracking is one of the most common types of cracking in concrete structures. Usingdifferent fibres is one of the ways to control and reduce cracks in concrete. Examining the relationshipbetween the characteristics of Plastic shrinkage cracking in concrete structures containing fibres isimportant in better understanding this type of cracking and reducing it. The present research examines thechanges in the severity of plastic shrinkage cracking in concrete mixtures under influenced of the additionof macro synthetic fibres. After determining proportions of concrete mixtures, macro polypropylene fibreswere used in amounts of ۰, ۰.۹, ۱.۸ and ۲.۷ kg/m۳. Plastic shrinkage cracking was evaluated according tothe ASTM C۱۵۷۹ standard method, and the geometric characteristics of cracking, including average crackwidth, crack length, and crack area, were determined using digital image analysis. The results showed thatthe change of the average crack width causes a change in the behaviour of the cracking length and area.Cracking length and area change with the change of average cracking width up to ۱۵% and ۸۶%,respectively. It has been seen that the change of average crack width has a greater effect on the change ofthe cracking area. After the average crack width reaches a certain amount, the increasing trend of thecracking area decreases. Also, it was observed that the change in average crack width is greater than itslength.

کلیدواژه ها

Concrete structures, Plastic shrinkage cracking, Cracking severity, Macrosynesthetic fibres, Average cracking width, Cracking length, Cracking Area.

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.