Effect of processing parameters on the morphology of α-phase in Ti-۶Al-۴V alloy during the two-step hot deformation
- سال انتشار: 1402
- محل انتشار: مجله شکل دهی مواد، دوره: 10، شماره: 3
- کد COI اختصاصی: JR_IJMF-10-3_007
- زبان مقاله: انگلیسی
- تعداد مشاهده: 91
نویسندگان
Hakim Sabzevari University
Materials and Metallurgical Engineering Department, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
Department of Materials and Polymer Engineering, Hakim Sabzevari University, Sabzevar, Iran
چکیده
The morphology of the α-phase in titanium alloys considerably affected their physical and mechanical properties. In this research, the effect of applied strain and inter-pass times on the morphology of the α-phase was studied in the two-step hot deformation process. Hot compression tests were performed at ۹۰۰ ºC and ۰.۰۰۱ s-۱ while the strains in the first and second passes were set as (first cycle: ۰.۶ and ۰.۳) and (second cycle: ۰.۳ and ۰.۶) respectively, with various inter-pass times. The work softening parameter obtained from the stress-strain curves showed that the proper time for globularization of α-layers for the first pass strain of ۰.۶ was ۲۴۰ s and for the second strain of ۰.۳ it was ۲۴۰ and ۳۰۰ s. Microstructure results indicated that the first pass strain of ۰.۳ and the inter-pass time of ۲۴۰ s were the optimum conditions for globularization of α layers.کلیدواژه ها
Ti-۶Al-۴V alloy, Two-step hot deformation process, Microstructureاطلاعات بیشتر در مورد COI