Study on microstructure and mechanical properties of rolled alloy 5083 H112 after heat treating at different temperatures
- سال انتشار: 1391
- محل انتشار: دومین کنفرانس بین المللی آلومینیوم
- کد COI اختصاصی: IIAC02_054
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1159
نویسندگان
Department of Materials Engineering, Isfahan University of Technology ۸۴۱۵۶-۸۳۱۱۱, Isfahan, Iran
Department of Materials Engineering, Isfahan University of Technology ۸۴۱۵۶-۸۳۱۱۱, Isfahan, Iran
Department of Materials Engineering, Isfahan University of Technology ۸۴۱۵۶-۸۳۱۱۱, Isfahan, Iran
Department of Materials Engineering, Isfahan University of Technology ۸۴۱۵۶-۸۳۱۱۱, Isfahan, Iran
چکیده
Generally control of micro structure for improvement of material properties is very important. Hence, several researches have been done to improve structure and mechanical behavior of materials in sub-micron grain size at recent years. Grain atomizing is an effective and economical method to improve the mechanical properties of materials. In this study a thickness reduction of about 85% was applied on Aluminum 5083 H112 sheet by cold rolling. Then samples were heat treated at different temperatures. The micro structure changes were tested by optical microscopes. In order to analyze the mechanical properties; the samples were applied to mono-axis tensile, hardness and wear tests. Also the investigation of fracture surface of samples after tensile tests and microstructure was done by SEM.The results showed that the critical temperature in micro-structure changes is 250 °c. Also at this temperature a static recrystalization takes place which starts at 200°c.The result of wear test showed that friction coefficient near to static recrystalization process increase slightly which in accordance with temperature increase it starts to decrease. Samples hardness by effect of heat treatment at 250°c, increase then it starts to decrease. Also the fracture surface results show that a mixture of tear ductile dimples at recrystalization temperature leads to rupture.کلیدواژه ها
recrystalization; Aluminum 5083 H112; hardness; structureمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.