Microstructure and hot deformation behavior of AlMg6 alloy produced by equal-channel angular pressing

  • سال انتشار: 1391
  • محل انتشار: دومین کنفرانس بین المللی آلومینیوم
  • کد COI اختصاصی: IIAC02_028
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 1925
دانلود فایل این مقاله

نویسندگان

Gholamreza Khalaj

Department of Materials Science and Engineering, Saveh Branch, Islamic Azad University, Saveh, Iran

Ali Nazari

Department of Materials Science and Engineering, Saveh Branch, Islamic Azad University, Saveh, Iran

Mohammad Javad Khalaj

Department of Materials Science and Engineering, Saveh Branch, Islamic Azad University, Saveh, Iran

Mohammad Mahdi Khaykha

Mechanical Engineering Group, Department of Engineering, Zabol university, Zabol. Iran.

چکیده

Experimental work carried out to assess the strain rate and temperature affected deformation behavior of equal-channel angular pressed (ECAPed) AlMg6 alloy. Elevated temperature compression test performed at temperatures ranged from 360 to 520 , four strain rate of 0.001, 0.01, 0.1 and 1s-1. The flow stress curves are displayed two kind of different behavior, which, at low temperatures or high strain rates, during the initial stage of deformation there is an increase in the flow stress, whereas, at high temperatures or low strain rates, flow curve decrease continuously from yield point due to occurrence of dynamic recrystallization phenomena. Activation energy of deformation is calculated 185.5 KJmol-1 for the alloy. Steady state strain rate sensitivity (SRS) parameters were calculated for the strain rate ratios of 1 2 (1:10), 2 3 (10/100). The increasing of the m values from 0.1 to 0.4 for the applied strain rate ratios of 2 3 (10/100) and 1 2 (1:10), respectively, is assumed to be the result of changing the deformation mechanism from recovery to recrystallization. The effects of number of passes and strain path have been studied on the mechanical and microstructural characteristics of this alloy.

کلیدواژه ها

Hot deformation, ECAP, Dynamic recrystallization, AlMg6 alloy

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.