Corrosion performance of an additive manufactured ۳۱۶L stainless steel in the concrete pore solution
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 87
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-20-1_002
تاریخ نمایه سازی: 7 اسفند 1402
چکیده مقاله:
Selective laser melting (SLM) is a manufacturing technique that can be used to create products with complex geometries and materials. This study investigated the microstructure and electrochemical behavior of SLM-processed ۳۱۶L stainless steel (SLM-fabricated ۳۱۶L SS) and a commercially wrought counterpart in a concrete pore solution. The results showed that SLMed ۳۱۶L SS had a finer microstructure with ultrafine cellular/columnar grains than the wrought counterpart. This was due to the high cooling rate of the SLM process. The SLM sample also had a higher charge transfer resistance and lower corrosion current densities than the wrought counterpart, indicating better corrosion performance in alkaline media. This could be attributed to the fabrication method of the SLM- fabricated sample, which prevents the formation of harmful phases and defects. These properties indicate an improved corrosion performance of the SLM sample over the wrought counterpart. As a result, SLM can be a promising fabrication method for producing corrosion-resistant materials.
کلیدواژه ها:
نویسندگان
Mahdi Yeganeh
دانشگاه شهید چمران اهواز
Hasan Shaeri Karimi
Shahid Chamran Unversity of Ahvaz
Seyed Reza Alavi Zaree
Shahid Chamran University of Ahvaz
Mostafa Eskandari
Shahid Chamran University of Ahvaz