Mechanical and Bioactive Properties of a Commercial Glass Carbomer: GCP Glass Fill
- سال انتشار: 1396
- محل انتشار: مجله تحقیقات دندانپزشکی، دوره: 9، شماره: 4
- کد COI اختصاصی: JR_AJDR-9-4_003
- زبان مقاله: انگلیسی
- تعداد مشاهده: 33
نویسندگان
چکیده
Background: Glass carbomers, such as GCP Glass Fill, are a type of GICs, which have nanosized apatite added to their composition. The manufacturer describes this material to have remineralizing properties. Objectives: This study aimed to evaluate the bioactivity of this material and the effect of finishing by thermocuring and gloss on its properties. Methods: Bioactivity was measured by Ca and PO۴ release studies, SEM, FT-IR, as well as EDX. Mechanical properties were measured by a compressive strength test. Results: Cements of all finishing types (with/without gloss and/or thermocuring) had comparable and acceptable initial compressive strengths. After an incubation period, all strengths decreased. Conclusions: Although GCP Glass Fill should be bioactive, no signs of bioactivity after incubation in SBF were observed. Moreover, the finishing conditions with Glass and thermocuring do not improve the mechanical properties of the cement. Therefore, this material is not superior to e.g. GICs.کلیدواژه ها
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.