The study of Oxidation Behavior of AISI ۴۳۹ Steel at the Presence of Manganese Oxides for the Application in Solid Oxide Fuel Cells
- سال انتشار: 1395
- محل انتشار: مجله شیمی فیزیکی و الکتروشیمی، دوره: 4، شماره: 2
- کد COI اختصاصی: JR_JPEM-4-2_003
- زبان مقاله: انگلیسی
- تعداد مشاهده: 44
نویسندگان
Department of Materials Science and Engineering, Ayatollah Amoli Branch ,Islamic Azad University, Amol, Iran.
Department of Materials Science and Engineering, Faculty of Engineering, Shahid Bahonar University of Kerman, Kerman, Iran.
Department of Materials Science and Engineering, Faculty of Engineering, Shahid Bahonar University of Kerman, Kerman, Iran.
چکیده
Long–term stability and oxidation resistance of AISI ۴۳۹ ferritic stainless steel used as interconnects in solid oxide fuel cells can be improved by use of a protective coating. In this study the pack cementation method was employed to coat AISI ۴۳۹ ferritic stainless steel with manganese. Isothermal oxidation was conducted at ۸۰۰ ºC for ۲۰۰ hours in static air to investigate the role of coating against oxidation. Cyclic oxidation was also performed for up to ۱۰۰ cycles at the oxidation temperature of ۸۰۰ °C. Formation of manganese oxides (MnFe۲O۴, Mn۳O۴ and Mn۲O۳) during oxidation tests improved oxidation resistance. The coated samples demonstrated lower mass gain in each test, indicating the coating layer could have act as a mass barrier against the outward diffusion of cations specially Cr.کلیدواژه ها
Oxidation, Solid oxide fuel cell, AISI ۴۳۹ ferritic stainless steel, Manganese, Interconnectاطلاعات بیشتر در مورد COI