Synthesis of titanium carbide nanopowder from sol gel derived precursor
- سال انتشار: 1398
- محل انتشار: دوازدهمین کنگره سرامیک ایران
- کد COI اختصاصی: ICC12_108
- زبان مقاله: انگلیسی
- تعداد مشاهده: 68
نویسندگان
Faculty of materials science and Engineering, Iran university of science and Technology, Tehran, Iran
Faculty of materials science and Engineering, Iran university of science and Technology, Tehran, Iran
Faculty of materials science and Engineering, Iran university of science and Technology, Tehran, Iran
ustralial national university Iran university of Science and Technology
چکیده
titanium carbide nanopowder was synthesized by sol–gel method using tetra-n-butyl orthotitanateas titanium source and saccharose as carbon source. The sol-gel processes have been controlledby ethyl aceto acetate. Yellowish sol was placed in air for ۲۴ h under continuous stirring to get agel. A dried gel was obtained after the gel was heated in a temperature range of ۱۱۰–۱۲۰ ℃ for۱.۵ h. When heat-treated at ۵۴۰ ℃, gels transformed into intimately mixed amorphous carbon andnanosized tetragonal TiO۲. Further heat treatments above ۱۰۰۰ ℃-۱۲۰۰ ℃ led to the formation ofmagneli phases. Increasing the temperature to ۱۳۰۰ ℃ and ۱۴۰۰ ℃ led to formation of titaniumcarbonitrides and pure titanium carbide. Powders were assessed using X-ray diffraction, X-rayfluorescence (XRF) analysis, Dynamic light scattering (DLS) and scanning electron microscopy.The average size of the TiC particles was found to be about ۴۰ nm.کلیدواژه ها
Sol-gel process, titanium carbide, nano powders, carbothermal nitridation.اطلاعات بیشتر در مورد COI