Study of the production possibility of thermal barrier coatings stabilized on the inconel ۷۳۸LC zirconia supper alloy with electrophoretic deposition method
- سال انتشار: 1402
- محل انتشار: یازدهمین کنفرانس بین المللی مهندسی مکانیک، مواد و متالورژی
- کد COI اختصاصی: MEMCONF11_001
- زبان مقاله: انگلیسی
- تعداد مشاهده: 197
نویسندگان
MSC, College of Allameh Hasanzadeh Amoli
چکیده
Zirconia coatings stabilized with ytteria are among heat barrier coatings and are used in airspace industry and gas turbines widely. Stability in high temperature working condition of these coatings has been always considered by researchers. In this work, application of zirconia coatings stabilized with ۸% wt. ytteria using electrophoretic deposition method in a solution containing acetone and ethanol (۳:۱) on the Inconel ۷۳۸ LC alloy substrate was investigated. In the present work, The applied dc voltage was varied from ۱۰ to ۸۰V.cm−۱ and also the deposition time was varied ۱-۵ min. Crack-free green ۸YSZ film deposited on IN۷۳۸LC substrates were dried at room temperature for ۱ day. The ۸YSZ deposits were viewed under a metallurgical microscope to determine the presence of cracks or other defects in the as deposited coatings after initial drying. The polished cross-sections of the porous specimens were observed in an optical microscope (OM) and and the surface morphology was characterized using a scanning electron microscope (SEM). The results showed that the effect of applied dc voltage during EPD on the weight of the deposit and in turn on the thickness of the coating obtained was studied. the increase in voltage results in increase of coating rate and consequently the increase of the coating thickness in a definite time. Furthermore, in the constant applied voltage, as the time goes on, the thickness of the coating increases but ultimately the rate of the thickness increase decreases. In optimized condition, the developed coatings in the average applied voltage (۲۵-۴۵), have more uniform surface morphology and thickness than other applied voltage.کلیدواژه ها
۸YSZ (۸% Yttria Stabilized Zirconia), thermal barrier coating, EPD, IN۷۳۸LC.مقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.