Studying the Structural and Optical Properties of Thin Compound Oxide Films Based on TiO۲: NiO: In۲O۳ Nanostructure

سال انتشار: 1402
محل انتشار: نشریه متدهای شیمیایی، دوره: 7، شماره: 11
کد COI اختصاصی: JR_CHM-7-11_005
زبان مقاله: انگلیسی
تعداد مشاهده: 38

نویسندگان

Physics Department, College of Science, University of Baghdad, Baghdad, Iraq

Laboratory of Materials for Energy and Environment, and Modeling (LMEEM), Faculty of Sciences, University of Sfax, B.P: ۱۱۷۱, ۳۰۳۸, Tunisia

چکیده

Spray pyrolysis has been used to fabricate different mixed TiO۲/NiO/In۲O۳ nanostructures. TiO۲/NiO/In۲O۳ has been structurally and optically explored using X-ray diffraction, field emission scanning electron microscopy, and UV-Vis spectroscopy. The particles analysis using X-ray diffraction had a polycrystalline structure and all of the observed peaks can be assigned to the samples with nanostructure, while FESEM reveals that they are very small, spherical, and range in size from ۱۴ to ۱۰۰ nm. The UV-Vis observed the edge of absorbance at about ۳۳۵-۳۰۵ nm; the energy band gap was calculated to be ۳.۳-۳.۵۸ eV. The absorbance in this area is caused by the creation of TiO۲/NiO/In۲O۳ nanoparticles. The synthesis of thin films was tested in gas sensor applications. The gas response of the tested samples to hydrogen sulfide gas at different operating temperatures was analysed. The thin film demonstrates that when the operating temperature got higher, sensitivity increased as well. With an increase in operational temperature, recovery and response times are slowed down.

کلیدواژه ها

TiO۲/NiO/In۲O۳, Nanostructure, Gas Sensor, H۲S Gas

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.