Optimization of Surface Treatment of GrayIron with Atmospheric-Pressure Plasma Jet
- سال انتشار: 1402
- محل انتشار: سومین کنفرانس بین المللی پژوهش ها و دستاوردهای نو در علوم، مهندسی و فناوری های نوین
- کد COI اختصاصی: SETBCONF03_137
- زبان مقاله: انگلیسی
- تعداد مشاهده: 109
نویسندگان
PhD in Atomic-Molecular Physics (Plasma Physics) from Arak University; Researchand Development Branch, PLASMA SATH GOSTAR AMIRKABIR (PSGAK) Company, Arak, ۳۸۱۴۹۵۵۶۲۸, Iran
چکیده
In this study, for the first time to our knowledge, the effect of different operationalparameters of an argon atmospheric-pressure plasma jet (APPJ) onmicrostructure, hardness and wettability of grey cast iron is investigated. Thesamples were treated by three different methods of argon APPJ treatment tooptimize the operating conditions. For this purpose, the surface modification isexamined using analyzing techniques namely, water contact angle (WCA)measurements for the wettability, and a Brinell hardness tester for the hardnessmeasurements. The microstructures of the samples were studied by opticalmicroscopy as well. Experimental results show that the hardness of grey cast ironcan be enhanced significantly by increasing the gas flow rate and treatment timeof argon APPJ and were optimum at ۱۵ standard litter per minute (SLM) and ۱۵minute (min), respectively. Moreover, the APPJ nozzle-grey cast iron distancewas the most influencing parameter for reducing the intrinsic hydrophilicity of thegray cast and was optimum at ۲cm.کلیدواژه ها
Gray iron, hardness, wettability, atmospheric-pressure plasma jetمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.