Effect of Input Heat of SMAW Process on Microstructure and Corrosion of Weld Metal API ۵L X۶۵ Steel Joints Coated with INCOLOY ۸۲۵ Superalloy
- سال انتشار: 1400
- محل انتشار: مجله علوم و مهندسی خوردگی، دوره: 11، شماره: 42
- کد COI اختصاصی: JR_ICAC-11-42_006
- زبان مقاله: انگلیسی
- تعداد مشاهده: 101
نویسندگان
چکیده
In this study, the effect of input heat of SMAW process on the microstructure and corrosion behavior of welded metal API ۵L X۶۵ steel joints coated with INCOLOY ۸۲۵ superalloy was investigated. Welding with input heat of ۱.۰۳, ۰.۹۹ and ۰.۹۴ kJ / mm was performed using E۷۰۱۸ filler metal by SMAW process. FESEM scanning light and electron microscopy was used to study the microstructure. Evaluation of corrosion behavior of weld metal was performed using TOEFL polarization test in ۳.۵% NaCl solution. The microstructural results showed that the needle ferrite in the weld metal microstructure decreased with increasing inlet heat. While the values of Wiedmann Statten ferrites are multifaceted and grain boundaries. It was found that increasing the inlet heat had a negative effect and reduced the corrosion resistance of the weld metal.کلیدواژه ها
X۶۵ steel, corrosion, electrode ۷۰۱۸, welding, SMAW Process, فولادX۶۵, خوردگی, الکترود ۷۰۱۸, جوشکاری, فرآیند SMAWاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.