Optimizing Corrosion Resistance Behavior of Vanadium Conversion Coating on Hot-Dip Galvanized Steel Substrate
- سال انتشار: 1396
- محل انتشار: مجله علوم و مهندسی خوردگی، دوره: 7، شماره: 26
- کد COI اختصاصی: JR_ICAC-7-26_003
- زبان مقاله: انگلیسی
- تعداد مشاهده: 108
نویسندگان
چکیده
Corrosion resistance of galvanized steel increased by optimizing operating conditions (pH, temperature and immersion time) of vanadium conversion coating. In order to evaluate the corrosion behavior of vanadium conversion coating, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization were used in ۳.۵%wt sodium chloride solution. The results showed the best performance of corrosion resistance at pH=۱.۵, temperature of ۴۵°C with ۱۵ minutes immersion time. The Polarization resistance increased from ۱۰۷۵(Ω.cm۲) for uncoated galvanized steel to ۵۴۲۷۷ Ω.cm۲ in the presence of vanadium conversion coating As well as the corrosion current density decreased from ۶.۳۶×۱۰-۶ A/cm۲ to ۰.۶۱۸۲×۱۰-۶ A/cm۲.کلیدواژه ها
Vanadium Conversion coating (VCC), Galvanized steel, Electrochemical Impedance Spectroscopy (EIS), Scanning Electron Microscopy (SEM), پوشش تبدیلی وانادیم, فولاد گالوانیزه, طیف سنجی امپدانس الکتروشیمیایی(EIS), میروسکوپ الکترونی روبشی(SEM).اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.