THERMAL STABILITY OF NANOSTRUCTURED Al-11.6Fe-1.3V-2.3Si ALLOY PRODUCED BY MECHANICAL ALLOYING AND HOT PRESSING METHODS
- سال انتشار: 1391
- محل انتشار: اولین همایش بین المللی و ششمین همایش مشترک انجمن مهندسی متالورژی ایران
- کد COI اختصاصی: IMES06_197
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1323
نویسندگان
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
چکیده
Thermal stability of nanostructured Al-11.6Fe-1.3V-2.3Si (wt.%) alloy was investigated. In this regard, the nanostructured Al-11.6Fe-1.3V-2.3Si alloy first produced by mechanical alloying (MA) and subsequent hot pressing (HP) of elemental powders. Structural evolution during the MA and HP were studied by X-ray diffraction (XRD). The density of hot pressed sample measured by Archimedes method. Hardness test was conducted by Vickers method at a load of 10 kg. In order to assess the thermal stability of produced alloy, hardness samples were annealed in air in a conventional furnace up to 100 h at 400°C, 500°C and 600°C. XRD results demonstrated that MA of elemental powders up to 60 h led to the formation of a nanostructured Al based solid solution. After HP, Al12(Fe,V)3Si phase precipitated in nanostructured Al matrix. Density measurement showed that the produced alloy had a relative density of ~97%. This alloy exhibit a high hardness value of 254 HV which remainsunchanged after 100 h exposure to 400°C, but decreased after annealing at 500°C and 600°C. Al12(Fe,V)3Si phase also remained stable in the Al matrix after 100 h annealing at 600°C.کلیدواژه ها
mechanical alloying, hot pressing, thermal stabilityمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.