Evolution of properties and densification behavior during sintering of brass Cu-20Zn prepared from prealloyed powder
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,193
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_181
تاریخ نمایه سازی: 8 بهمن 1391
چکیده مقاله:
The aim of this study is the necessity of applying optimal fabrication condition of Cu-20Zn alloy to increase the capability of controlling its properties, since physical and mechanical properties and microstructural changes of this alloy depend on trivial changes in sintering temperature. For this purpose, water atomized prealloyed brass powder, with average particle size of 40 to 100 μm, was compacted under pressure of 600 MPa and sintered at the temperature range of 900 to 950°C in Aratmosphere. The results of the density and dimensional changes measurement, hardness and impact energy testing show that the optimum sintering temperature is 930°C. Moreover, microstructural and fractographic analysis is in a good agreement with obtained physical and mechanical properties. The amount of liquid phase, which depends on sintering temperature, results in different load bearing cross section areas, also it affects the type of fracture morphology (transgranular or intergranular
کلیدواژه ها:
نویسندگان
A. Sabahi Namin
Department of Materials Engineering, Sahand University of Technology, P.O. Box ۵۱۳۳۵-۱۹۹۶, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :