Tribological performance of Steel/TiC nanocomposite produced by friction stri processing

سال انتشار: 1391
محل انتشار: اولین همایش بین المللی و ششمین همایش مشترک انجمن مهندسی متالورژی ایران
کد COI اختصاصی: IMES06_131
زبان مقاله: انگلیسی
تعداد مشاهده: 1116

نویسندگان

University of Tehran

چکیده

In this study, the almost new processing technique, friction stir processing (FSP) was employed to produce nanocomposite surface layers on mild steel. Nano-sized TiC particulates were introduced to the stir zone by means of a pre-made groove. A tungsten carbide tool was used to plasticize the mild steel substrate. The process transformed the original pearlite microstructure to acicular-type ferrite, resulting in significant increase in surface hardness. This surface hardening produced a significant benefit for friction and wear behavior of the steel as measured by unidirectional sliding pin-on-disk testing. Under sliding, FSP reduced friction coefficient and wear rate and increase wear properties about four times more than that of the as-received mild steel. The surface nano-composite layer produced by four FSP passes showed superior wearresistance; this is attributed to its greater micro hardness value (due to presence of finer matrix grains and uniform dispersion nano-sized TiC particles

کلیدواژه ها

Metal-matrix nanocomposite, FSP, Tribology, Friction

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.