INFLUENCE OF PHOSPHORUS ADDITION ON THE MICROSTRUCTURE OF IN-SITU Al-25 WT.% Mg2Si COMPOSITE
- سال انتشار: 1391
- محل انتشار: اولین همایش بین المللی و ششمین همایش مشترک انجمن مهندسی متالورژی ایران
- کد COI اختصاصی: IMES06_109
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1399
نویسندگان
Imam Khomeini International University, Qazvin, Iran
school of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, P.O. Box: ۱۴۳۹۵-۷۳۱, Iran
چکیده
In current research, the effects of different concentrations of P (0, 0.05, 0.1, 0.3, 0.5, 0.7 and 1 % wt.) on the microstructures of Al-25%wt. Mg2Si composite have been investigated. Microstructural examination was carried out by using optical and scanning electron microscopy (SEM). As-cast microstructure analysis of the composite indicated that the primary Mg2Si phases are very coarse with average size of 200μm. Also the results show that P addition changes the morphology of primary Mg2Sifrom irregular to polygonal or spherical shapes and decreases size of primary Mg2Si particles from200μm to 20 μm in 1%wt. added P specimen. Furthermore, the morphology of eutectic Mg2Si phases changes from fibriform to short fibriform or dot-like. With the addition of P, it reacts with Al to produce particles of AlP phase. The AlP particles can be appropriate sites for heterogeneous nucleation of Mg2Si. It is believed that P addition has strong influence on the nucleation process of primary Mg2Si particles and the subsequent formation of the α-Al phase and the eutectic matrix.کلیدواژه ها
Al/Mg2Si; Phosphorus; Modification; Castingمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.