Effect of Combining Hydraulic and Phosphate Bonds on Alumina-Spinel Low Cement Castables
- سال انتشار: 1387
- محل انتشار: مجله ی بین المللی انجمن آهن و فولاد ایران، دوره: 5، شماره: 1
- کد COI اختصاصی: JR_ISSIRAN-5-1_005
- زبان مقاله: انگلیسی
- تعداد مشاهده: 119
نویسندگان
Department of Materials Engineering, Isfahan University of Technology (IUT), Isfahan, ۸۴۱۵۶-۸۳۱۱۱, Iran
Department of Materials Engineering, Isfahan University of Technology (IUT), Isfahan, ۸۴۱۵۶-۸۳۱۱۱, Iran
Department of Materials Engineering, Isfahan University of Technology (IUT), Isfahan, ۸۴۱۵۶-۸۳۱۱۱, Iran
چکیده
A basic alumina-spinel low cement castable (LCC) composed of sintered bauxite, reactive alumina, calcined alumina, calcined magnesia, microsilica, and high alumina refractory cement was prepared (castable A) to which ۵% sodium hexa-meta phosphate was later added (castable B) to prepare samples for heat treatment at ۱۱۰ºC, ۹۰۰ºC, and ۱۴۰۰ºC. Bulk Density (BD), Apparent Porosity (AP), and Cold Crushing Strength (CCS) were measured and XRD and SEM studies were performed. It was shown that after heat treating at ۱۱۰ºC, CCS of castable B increased by more than ۳ times while its AP value was less than half that of castable A. The main difference between the two samples was found to lie in the presence of Mg۲P۲O۷ and AlPO۴.۲H۲O which are responsible for increases in CCS. At the temperature range of ۸۰۰-۱۰۰۰ºC where the hydraulic bond reverses to the dehydrated condition and castable A becomes weak with high porosity, castable B showed a CCS value of more than ۴ times. Needles of magnesium phosphate were found to be responsible for reinforcing the microstructure of castable B at ۹۰۰ºC. After firing at ۱۴۰۰ºC, castable B showed extraordinary CCS values of up ۱۰۰ MPa (about ۱۰۰۰ Kg/Cm۲), ۵ times stronger, and AP% of below ۱/۵ times that of castable A. The phases present after firing were alumina, Al۲O۳, spinel, MgAl۲O۴, calcium phosphate, Ca۳ (PO۴)۲ and Enstatite, and MgSiO۳. Magnesium phosphate melted at ۱۳۰۰-۱۴۰۰ºC and aided the formation of ceramic bonds. The Ca coming from calcium aluminate cement reacted with phosphate and developed refractory calcium phosphate.کلیدواژه ها
Powders-solid state reaction, Microstructure, Strength, Spinels, Refractoriesاطلاعات بیشتر در مورد COI