Dynamic Recrystallization by Necklace Mechanism During Hot Deformation of ۳۱۶ Stainless Steel
- سال انتشار: 1386
- محل انتشار: مجله ی بین المللی انجمن آهن و فولاد ایران، دوره: 4، شماره: 1
- کد COI اختصاصی: JR_ISSIRAN-4-1_003
- زبان مقاله: انگلیسی
- تعداد مشاهده: 182
نویسندگان
Department of Materials Engineering, Isfahan University of Technology,.Isfahan, ۸۴۱۵۶-۸۳۱۱۱, Iran
Department of Materials Engineering, Isfahan University of Technology,.Isfahan, ۸۴۱۵۶-۸۳۱۱۱, Iran
Department of Materials Engineering, Isfahan University of Technology,.Isfahan, ۸۴۱۵۶-۸۳۱۱۱, Iran
چکیده
The aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (DRX). The material used is ۳۱۶ stainless steel. In order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of ۹۵۰-۱۱۰۰ °C with strain rates of ۰.۰۱-۱s-۱. The result shows that at the temperature of ۱۰۰۰ °C with the strain rate of ۰.۱ s-۱, DRX developed by necklace mechanism, it is far from completeness over the steady state stress. By contrast the hardness increased by development of DRX. The final microstructure is very heterogeneous and comprises of very fine and coarse grains due to the occurrence of partial DRX. The results also show that the necklace structure developed by increasing Zener-Hollomon parameter (Z).کلیدواژه ها
Dynamic recrystallization, NecklaceMechanism, ۳۱۶ Stainless Steelاطلاعات بیشتر در مورد COI