X-ray diffraction peak profile analysis of maraged Fe-Ni-Mn steels
- سال انتشار: 1389
- محل انتشار: مجله ی بین المللی انجمن آهن و فولاد ایران، دوره: 7، شماره: 2
- کد COI اختصاصی: JR_ISSIRAN-7-2_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 56
نویسندگان
Faculty of Materials Engineering, Sahand University of Technology, P.O. Box ۵۱۳۳۵-۱۹۹۶, Tabriz, Iran
Faculty of Materials Engineering, Sahand University of Technology, P.O. Box ۵۱۳۳۵-۱۹۹۶, Tabriz, Iran
Faculty of Materials Engineering, Sahand University of Technology, P.O. Box ۵۱۳۳۵-۱۹۹۶, Tabriz, Iran
چکیده
X-ray diffraction peak profile analysis was used to identify changes in the lattice distortions during isothermal aging of Fe-۱۰Ni-۷Mn (wt. %) maraging steel. Integral peak breadths were analyzed using classical Williamson-Hall equation taking the elastic anisotropy into account. It was found that substantial lattice distortions rise during precipitation hardening which depend strongly on the specific Young’s modulus of a given crystallographic direction. After normalizing by elastic stiffness, the magnitude of average lattice distortions increased reasonably in accordance with age hardening.کلیدواژه ها
X-ray diffraction, peak breadth, maraging, Precipitation, lattice strainاطلاعات بیشتر در مورد COI