The effect of quenching media and annealing temperature on graphitization transformation kinetic of CK۱۰۰ tool steel

  • سال انتشار: 1390
  • محل انتشار: مجله ی بین المللی انجمن آهن و فولاد ایران، دوره: 8، شماره: 1
  • کد COI اختصاصی: JR_ISSIRAN-8-1_006
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 131
دانلود فایل این مقاله

نویسندگان

S. Rounaghi

Department of Materials Engineering, Ferdowsi University of Mashhad, Mashhad, Iran. P.O.Box No: ۹۱۷۷۵-۱۱۱۱

A. Kiani-Rashid

Department of Materials Engineering, Ferdowsi University of Mashhad, Mashhad, Iran. P.O.Box No: ۹۱۷۷۵-۱۱۱۱

چکیده

In this research, graphitization transformation of a commercial hypereutectoid steel called CK۱۰۰ was studied by the dilatometric experiments at the range of ۶۰۰ – ۷۰۰ °C from prior martensitic structure. Also the effect of quenching media on the initial graphitization time and completion of transformation has been discussed. Also, graphitization transition from the different prior microstructures was studied using microscopic observations. Analyzing dilatometric data acquisitions confirmed good following results from Johnson–Mehl–Avrami equation. By calculating Avrami exponent, following of transformation kinetic from diffusion controlled nucleation and growth was resulted. Also, the minimum time for completion graphitization transformation was concluded about ۴۵ hrs relative to the water quenched specimen after annealing at ۶۷۰ °C.

کلیدواژه ها

Graphitization, CK۱۰۰, Microstructure, martensite

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.