Microstructural Evolution of X۴۵CrNiW۱۸۹ Valve Steel During Hot Deformation

سال انتشار: 1394
محل انتشار: مجله ی بین المللی انجمن آهن و فولاد ایران، دوره: 11، شماره: 1
کد COI اختصاصی: JR_ISSIRAN-11-1_006
زبان مقاله: انگلیسی
تعداد مشاهده: 167

نویسندگان

Metallurgy & Material Dept., Golpayegan University of Technology, P.B.: ۸۷۷۱۷-۶۵۶۵۱, Golpayegan, Iran.

چکیده

The hot compression tests were carried on X۴۵CrNiW۱۸۹ valve steel (X۴۵) in the temperature range of ۱۰۰۰– ۱۲۰۰ °C and the strain rate range of ۰.۰۰۴ – ۰.۵ s-۱ in order to study the high temperature softening behavior of this steel. For the exact prediction of flow stress, the effective stress-effective strain curves were obtained from experiments under various conditions. On the basis of experimental results, the dynamic recrystallization fraction (DRX), austenite grain size (AGS), hot deformation and activation energy behavior were investigated. It was found that the calculated results were in a good agreement with the experimental flow stress and the microstructure of the steel for different conditions of hot deformation.

کلیدواژه ها

X۴۵CrNiW۱۸۹, Valve, compression, Recrystallization, deformation

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.