Failure Modes Analysis System in Casting Parts by Process Failure Mode Effects Analysis (PFMEA) Method
- سال انتشار: 1401
- محل انتشار: مجله ی بین المللی انجمن آهن و فولاد ایران، دوره: 19، شماره: 2
- کد COI اختصاصی: JR_ISSIRAN-19-2_006
- زبان مقاله: انگلیسی
- تعداد مشاهده: 78
نویسندگان
Research and Development Manager, Ghaltak Sazan Sepehan
چکیده
Improving the level of quality of products and services provided by companies is the first and main factor of development to get a major market share. In this regard, the failure mode and effects analysis are an effective method to improve the quality and reduce waste in products. To eliminate the existing defects, especially protrusion of the melt from the casting parts, the analysis of potential failure modes based on the multiplication of three numbers of intensity, occurrence and detect was used. The results of the study showed that to reduce the melting run out defect, the most important potential for failure is the lack of skills and experience of personnel in assembly, inadequate quality of raw materials, non-compliance with continuous casting with a risk priority number of ۳۰۰,۴۰۰,۴۵۰, respectively. Continuous training, preparation of a checklist for input items and controlling the molding continuity reduced waste run outs defect by ۷۰%.کلیدواژه ها
Failure Effects, Melting Run Out, FMEAاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.