Preparation, Identification, and Evaluation of the Thermal Properties of Novolac Resins Modified with TiO۲, MgO, and V۲O۵ Oxides

سال انتشار: 1403
محل انتشار: مجله مکانیک سازه های پیشرفته کامپوزیت، دوره: 11، شماره: 1
کد COI اختصاصی: JR_MACS-11-1_001
زبان مقاله: انگلیسی
تعداد مشاهده: 239

نویسندگان

Department of Chemistry, Faculty of Sciences, Zanjan University, Zanjan, Iran

چکیده

It is essential to improve thermal insulation. In this study, titanium dioxide (TiO۲), magnesium oxide (MgO), and vanadium pentoxide (V۲O۵) were used as additives to modify phenolic novolac resin by the solution mixing method. Different weight percentages of resin nanoparticles (NPs) were added, and nanocomposites with different weight percentages were prepared. These nanocomposites were investigated by field emission scanning electron microscope (FE-SEM), X-ray diffraction spectroscopy (XRD), and oxyacetylene flame test (OFT). The FE-SEM images showed that the NPs were dispersed on the surface of the novolac resin at low concentrations. However, at high concentrations, the dispersion was suppressed in some cases by aggregation in the nanocomposites. The OFT test proved that by increasing the content of NPs in the nanocomposite, the back surface temperature of the sample decreased, thus improving the thermal insulation properties.

کلیدواژه ها

Novolac resin, Titanium Dioxide, Magnesium oxide, Vanadium pentoxide, Nanocomposite, Thermal insulation

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.