Investigating the Hot Extrusion Method for Cermet Powder Mixtures
- سال انتشار: 1402
- محل انتشار: مجله اوراسیا تحقیقات در شیمی، پزشکی و نفت، دوره: 2، شماره: 4
- کد COI اختصاصی: JR_EJCMPR-2-4_002
- زبان مقاله: انگلیسی
- تعداد مشاهده: 67
نویسندگان
Department of Research and Development, UOP, England
چکیده
The process of hot extrusion of very fine cemented carbide powder with a combination of softener has been known for many years. This method has been successfully used for cermet’s to make simple prismatic shapes that have a large length to cross-sectional area ratio. Cylindrical and quadrangular shapes and other sections can be easily made with this method, even making pipes is also possible. Depending on the plasticizer used (for example, polystyrene with the addition of dimethyl and diphenyl ether), the extrusion process requires temperatures between ۱۶۰ and ۱۷۵ degrees Celsius (۳۲۰- and ۳۵۰-degrees Fahrenheit). The process of complete and slow sticking under vacuum before full sintering is necessary and even vital to avoid stretching (from casting defects, from sagging), breaking or very small porosity. Twisting of bodies produced by extrusion similar to what happens in the plastic industry is acceptable for this process. In order to produce a high-quality product, hot pressing is necessary.کلیدواژه ها
Hot Extrusion Method, Cermet Powder Mixtures, Polystyrene, Plastic Industriesاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.