TRANSFORMATION BEHAVIOR OF NiTi SHAPE MEMORY ALLOYS TREATED BY THERMOMECHANICAL PROCESSING USING DSC
- سال انتشار: 1387
- محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 5، شماره: 4
- کد COI اختصاصی: JR_IJMSEI-5-4_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 27
نویسندگان
چکیده
Abstract: In the present study the effect of thermomechanical treatment (cold work and annealing) on the transformation behavior of NiTi shape memory alloys was studied. Differential scanning calorimetry was used to determine transformation temperature and its relation to precipitates and defects. Three alloys including Ti-۵۰.۳at.% Ni, Ti-۵۰.۵at.% Ni (reclamated orthodontic wires) and ۵۰.۶at.% Ni alloy were annealed at ۶۷۳ K and ۷۷۳ K for ۳۰ and ۶۰ min after ۱۵% cold rolling. It was found that the transformation characteristics of these alloys are sensitive to annealing treatment and composition. The temperature range of transformation is broadened during cold working and after subsequent annealing, the intermediate phase was appeared. The peaks become sharper and close together on each cooling and heating cycle with increasing annealing temperature and timeکلیدواژه ها
NiTi; Shape memory alloy; Thermomechanical treatment; Cold working; Annealing; DSC.اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.