EFFECT OF SILICON CONTENT ON THE STRAIN HARDENING OF DUAL-PHASE STEELS
عنوان مقاله: EFFECT OF SILICON CONTENT ON THE STRAIN HARDENING OF DUAL-PHASE STEELS
شناسه ملی مقاله: JR_IJMSEI-5-4_006
منتشر شده در در سال 1387
شناسه ملی مقاله: JR_IJMSEI-5-4_006
منتشر شده در در سال 1387
مشخصات نویسندگان مقاله:
A.Nouri
Sh.Kheirandish
H. Saghafian
خلاصه مقاله:
A.Nouri
Sh.Kheirandish
H. Saghafian
Abstract: In the current work, the strain hardening behavior of dual-phase steels with different silicon content (۰.۳۴-
۲.۲۶ Wt. %) was examined using the modified Crussard-Jaoul analysis. It was shown that these dual-phase steels
deform in two stages over a uniform strain range. Each stage exhibited a different strain hardening exponent varying
with silicon content. At the first stage, work hardening exponent remind significantly constant, while during the second
stage, it decreased with increasing silicon content from ۰.۳۴% to ۱.۵۱% and then increased for the higher silicon
contents (۱.۵۱% to ۲.۲۶%). It was found that the strain hardening behavior of these steels was predominantly affected
by the volume fraction of martensite at low silicon contet and the ferrite strengthening induced by silicon at the higher
silicon content. The effect of silicon content on the volume fraction of martensite and tensile properties were also
considered.