INVESTIGATION OFELECTRICALAND MECHANICALPROPERTIES OFTETRAGONAL/CUBIC COMPOSITE ELECTROLYTES PREPARED BYIMPREGNATION OFCUBIC ZIRCONIAWITH ZIRCONIASOLUTION
- سال انتشار: 1389
- محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 8، شماره: 1
- کد COI اختصاصی: JR_IJMSEI-8-1_002
- زبان مقاله: انگلیسی
- تعداد مشاهده: 52
نویسندگان
چکیده
Abstract: Zirconia solid electrolytes with nonequilibrium composite structure were prepared by impregnation of a porous ۸YSZ matrix with a solution of Zirconia. Microstructures were characterized by XRD and SEM. The electrical properties were studied by impedance spectroscopy as a function of temperature. Biaxial flexural strength and fracture toughness of composite samples were measured by ring on ring and Vickers microhardness indentation methods respectively. The microstructures of the composite electrolytes were composed of cubic grains surrounded by tetragonal second phase grains. It was shown that the electrical and mechanical properties of the prepared electrolyte can be adjusted by controlling the amount of doped zirconia. Increasing the amount of doped zirconia increases the tetragonal phase content which improves fracture toughness and fracture strength. In addition, increasing tetragonal phase content of the composite electrolytes decreases the conductivity at high temperatures while the situation is reversed at low temperatures.کلیدواژه ها
Keywords: Zirconia, Fuel Cell, Composite Electrolyteاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.