EFFECT OF SUPERSOLIDUS LIQUID PHASE SINTERING ON THE MICROSTRUCTURE AND DENSIFICATION OF THE Al-Cu-Mg PREALLOYED POWDER

  • سال انتشار: 1390
  • محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 8، شماره: 2
  • کد COI اختصاصی: JR_IJMSEI-8-2_002
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 141
دانلود فایل این مقاله

نویسندگان

H. Momeni

H. Razavi

S. G. Shabestari

چکیده

Abstract: The supersolidus liquid phase sintering characteristics of commercial ۲۰۲۴ pre-alloyed powder was studied at different sintering conditions. Pre-alloyed ۲۰۲۴ aluminum alloy powder was produced via air atomizing process with particle size of less than ۱۰۰ µm. The solidus and liquidus temperatures of the produced alloy were determined using differential thermal analysis (DTA). The sintering process was performed at various temperatures ranging from the solidus to liquidus temperatures in dry N۲ gas atmosphere for ۳۰ min in a tube furnace. The maximum density of the ۲۰۲۴ aluminum alloy was obtained at ۶۱۰ºC which yields parts with a relative density of ۹۸.۸% of the theoretical density. The density of the sintered samples increased to the maximum ۹۹.۳% of the theoretical density with the addition of ۰.۱ wt. %Sn powder to the ۲۰۲۴ pre-alloyed powder. The maximum density was obtained at ۱۵% liquid volume fraction for both powder mixtures.

کلیدواژه ها

Keyword: Al-Cu-Mg Aluminum Alloy, Supersolidus Liquid Phase sintering, Fractional grain boundary coverage,Densification

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.