INVESTIGATING SHRINKAGE CHANGES OF NATURAL POZZOLAN BASED GEOPOLYMER CEMENTPASTE

  • سال انتشار: 1390
  • محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 8، شماره: 3
  • کد COI اختصاصی: JR_IJMSEI-8-3_007
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 73
دانلود فایل این مقاله

نویسندگان

E. Najafi Kani

A. Allahverdi

چکیده

Shrinkage behavior of a geopolymer cement paste prepared from pumice-type natural pozzolan was studiedby changing parameters of chemical composition including SiO۲/Na۲O molar ratio of activator and total molar ratiosof Na۲O/Al۲O۳, and H۲O/Al۲O۳. For investigating the effect of curing conditions on shrinkage, hydrothermal curingwas also applied. The obtained results clearly revealed the governing effect of chemical composition on shrinkage.Mixes with different Na۲O/Al۲O۳ molar ratios exhibited different shrinkage behavior due to variations made inSiO۲/Na۲O molar ratio. Application of hydrothermal curing after a ۷-day period of precuring in humid atmospherealso showed strong effect on shrinkage reduction.

کلیدواژه ها

Geopolymer cement, Shrinkage, Chemical Composition, Curing, Natural Pozzolan

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.